TiO2 NRs:The TiO2 NRs were synthetized by using the
hydrothermal method as previously reported by Liu and
Aydil.21 0.4 mL of titanium butoxide was added into the
mixture containing 9 mL of deionized water and 9 mL of
concentrated hydrochloric acid (36%-38% by weight) slowly.
After stirring for 30 min,the as-prepared mixture was put into a
25 mL Tefl on-lined stainless steel autoclave.Four pieces of
FTO glass were placed at an angle against the wall of the
Teflon,linear with the conducting side facing down.The
hydrothermal synthesis was conducted at 190°C for 1.5− 3h in
an electric oven.
The morphology and microstructure of the TiO2
nanostuctures were examined by a scanning electron microscope
(LEO 1530 SEM),and transmission electron microscopy
(TEM,Hitachi HF2000 and JEOL 4000EX).Phase identification of TiO2
was conducted by X-ray diffraction (X’Pert PRO,PANalytical).

TiO2 NRs：采用上述报告的提到的方法通过LIU和Aydil进行水热法合成,在含有9毫升的去离子水和9毫升的浓盐酸（36％-38％）的混合物中缓慢地加入210.4毫升丁醇钛缓慢地.搅拌30分钟后,将混合物在放在不锈钢高压釜中,然后加入25毫升TEFL.将四块FTO玻璃在聚四氟乙烯器壁内侧依次地按照导电侧朝下的角度放置.然后在190℃的电烘箱进行水热合成,经过1.5-3h后,由扫描型电子显微镜（LEO 1530 SEM）,透射电子显微镜（TEM,日立HF2000和JEOL4000EX）观察TiO2形态和结构,再通过X-射线衍射对TiO2进行相（阶段）鉴定（X’Pert PRO,帕纳科）.
说明：
1.有问题我们可以一起探讨
2.我电气出身,对化学专业名字不是很熟悉,您再按照符合意思翻译一下
3.您发过来的英文本身有的句子没有断开符号
4.括号里面是个人觉得合适的翻译,但是不知道有没有这样的专业名词
4.附上经过调整的英文资料
TiO2 NRs: The TiO2 NRs were synthetized by using the hydrothermal method as previously reported by Liu and Aydil. 210.4 mL of titanium butoxide was added into the mixture containing 9 mL of deionized water and 9 mL of concentrated hydrochloric acid (36%-38% by weight) slowly. After stirring for 30 min, the as-prepared mixture was put into a 25 mL Tefl on-lined stainless steel autoclave. Four pieces of FTO glass were placed at an angle against the wall of theTeflon, linear with the conducting side facing down. The hydrothermal synthesis was conducted at 190°C for 1.5− 3h inan electric oven. The morphology and microstructure of the TiO2 nanostuctures were examined by a scanning electron microscope(LEO 1530 SEM), and transmission electron microscopy(TEM, Hitachi HF2000 and JEOL 4000EX). Phase identification of TiO2 was conducted by X-ray diffraction (X’Pert PRO, PANalytical).