Fig.7 shows 3D images and surface roughness of the Siwafer by AFM to compare the unimplanted with implanted surface.Roughness of Si-wafer before N+ ion implantation is about 6 Å while it reduced to about 3 Å after implantation.The lowest surface roughness was obtained on the sample implanted with 1×1017 N cm−2 dose.This result means that the nitrogen ion implantation by PSII causes surface morphology change together with improvement in mechanical properties of trivalent chromium surface.
PSII：等离子体源离子注入
Fig.7 shows 3D images and surface roughness of the Siwafer by AFM to compare the unimplanted with implanted surface.Roughness of Si-wafer before N+ ion implantation is about 6 Å while it reduced to about 3 Å after implantation.The lowest surface roughness was obtained on the sample implanted with 1×1017 N cm−2 dose.This result means that the nitrogen ion implantation by PSII causes surface morphology change together with improvement in mechanical properties of trivalent chromium surface.
PSII：等离子体源离子注入
图7显示的是原子力显微镜下硅片在注入氮离子前后的三维立体和表面粗糙维度对比.在氮离子注入前的表面粗糙度是6 Å,而在植入后则缩减为3 Å.最底层的粗糙度是对样本植入了1×1017 N平方厘米的剂量后取得的.这种结果表明：通过等离子体源离子注入的氮离子会引起表面结构形态的变化,同时对三价铬表面的机械性能得以改善.
英语翻译Fig.7 shows 3D images and surface roughness of the Siwaf
英语翻译The average surface roughness inside the microchannels w
英语翻译Fig.3 shows the DR UV–vis spectra of the (Co,H)-Y,the (C
英语翻译Fig.2 shows that the level of the input power flow decre
英语翻译Fig.11a shows the velocity profiles of the plane paralle
英语翻译Fig.12 shows the simulation results for 45º and -45
英语翻译Fig.3 shows the FPGA-internal block diagram.The three in
英语翻译Table 2 and Fig.3 show the influences of particle size a
英语翻译(3) Sudden turning Fig.18 shows the comparison between c
英语翻译Thus,the opposite effects of surface-lying and partially
英语翻译The increased surface hardness and wear resistance of el
英语翻译The 1H NMR spectra of complexes 1 and 2 are shown in Fig